Austenitic steels 
The heat resistance of austenitic steels is higher than that of pearlitic and 
martensitic steels and is used at temperatures above 600ºС. The main alloying elements 
are chromium and nickel. Sometimes nickel is replaced by other austenite-forming 
elements - Mo; Nb; Ti; Al; W. 
These form carbides and increase heat resistance. 
The heat resistance of austenitic steels is increased by quenching and aging: For 
example, for steel 10X11N20T3R quenching at 110-1170ºС and aging at a temperature 
of 750ºС for 15-25 hours. 
Austenitic steels have high plasticity, weld well. But it is worked and sheared 
under harder pressure. 


73 
Various cutting, deforming and measuring tools are made from tool steels and 
alloys. Various tools are used in mechanical engineering, and the quality of the tools 
has a great impact on the quality of the manufactured product and labor productivity. 
Tool steels must have high hardness and corrosion resistance. To achieve high 
hardness, tool steels contain 0.7...1.2% carbon. 
Tool steels are classified according to their application and properties. 
According to Yu.G.Geller's proposal, tool steels are divided into non-heat-resistant, 
heat-resistant and high-heat-resistant steels. 
The heat resistance of steel is expressed by the temperature at which its hardness 
decreases. 
Non-heat-resistant steels begin to lose the hardness achieved during tempering 
at 200-300 

C, semi-resistant steels at 300-500 

C and heat-resistant steels at 500-625 

happens. 
In addition, tool steels: 
a) steels with high hardness and corrosion resistance; 
b) is divided into steels with high viscosity. 
Steels of the first (a) group contain 0.7...1.5% carbon, and steels of the second 
(b) group contain 0.4...0.7% carbon. 
Tool steels by application: 
a) for cutting tools; 
b) for cold deformation stamps; 
c) divided into steels for hot deformation stamps; 
g) divided into steels for measuring instruments. 
Requirements for steels 

Yüklə 5,26 Mb.

Dostları ilə paylaş:
1   ...   26   27   28   29   30   31   32   33   ...   74




Verilənlər bazası müəlliflik hüququ ilə müdafiə olunur ©azkurs.org 2024
rəhbərliyinə müraciət

gir | qeydiyyatdan keç
    Ana səhifə


yükləyin