Fergana polytechnic insitute mechanical engineering faculty department of mechanical engineering and automation

Figure 1. 
Microscopic appearance of cast iron 
a)
gray cast iron with pearlite (Fig. 1, g) is composed of pearlite and plate -like 
graphite. 
b)
gray cast iron with pearlite-ferrite (Fig. 1, d) is composed of pearlite, ferrite 
and plate graphite. 
d)
Ferritic gray cast iron (Fig. 1, e ) is composed of plate graphite with ferrite. 
Malleable cast iron is obtained by softening white cast iron in a special way. 
They are called malleable because their plasticity is higher than that of gray cast 
iron. In ductile iron, carbon is in the form of free ductile graphite. Malleable cast 
irons, in turn, are pearlite (photo j) and ferrite (photo z). 
Very fine cast irons are obtained by adding a small amount of magnesium to 
the molten iron before casting it. The graphite released as a result of this process is 
spherical. Therefore, the structures of very refined cast irons consist of spherical 
small graphite grains with ferrite (Fig. 21, 
i ).
WORK PROCEDURE.
1. After adjusting the illumination using the diaphragm and light filters of the 
microscope, the necessary magnification is selected. 

---

155 
2. The examined samples are placed one after the other on the subject table of 
the microscope as shown in the previous laboratory work and observed under the 
microscope. 
3. Using the microstructure atlas, the structural elements of the examined steel 
and cast iron are carefully viewed from the photographs. Then, the equilibrium state 
microstructures of the cast iron samples are viewed and studied at 200 to 500 times 
magnification. 
4. Each microstructure viewed under the microscope is drawn on a paper with 
a diameter of 50 mm or a square paper with a size of 60x60 mm. 
5. At the bottom of each drawn microstructure, how much it is enlarged, the 
name of the alloy, its chemical composition and structure are indicated. 
6. In each drawn microstructure, its phase, structure composition and their 
names are indicated by arrows. 
An "iron-cementite" phase diagram is drawn, vertical lines corresponding to 
the investigated alloys are drawn, and the transformation process that occurs when 
the alloys are cooled is recorded.