Fergana polytechnic insitute mechanical engineering faculty department of mechanical engineering and automation

brasses, 
bronzes, copper-nickel alloys. 
Depending on the technological function: deformable, 
cast. Depending on the refinement after mechanical processing: those that are polished, 
those that are not polished by thermal treatment. 
If zinc (zinc) is the main alloying (element) component in a copper alloy, the 
alloy is called brass. There are two-component and multi-component . Two-component 
ones are marked L90: 90% copper, the rest is zinc. 
Multi-component: LANKMts 75-2-2.5-0.5-0.5 is 75% Cu; 2% - Al; 2.5% - Ni; 
0.5% - Si; 0.5% manganese; The rest is zinc. 
In practice, brasses containing up to 45% zinc are used. 
Fe is added to improve mechanical and technological properties. Dark gray 
deteriorates plasticity . Phosphorus increases hardness and greatly reduces plasticity. 
Al; Si; Mn does not affect the calculation. Al to increase corrosion resistance; Si; Mn; 
Ni is added. The addition of tin facilitates mechanical work and increases resistance to 
wear and tear: LO 90-1. 
Bronzes. 
In the copper alloy, the main components are tin Al; beryllium; Si; if 
lead called alloy bronze. Marking: BR OF 6.5-0.15 contains 6.5% - tin, 0.15% - 
phosphorus; The rest is copper. 
Alloys of copper with nickel and other alloying elements are different types of 
bronze, they are called melchior, neusilber, kunial, copelium. For example, melchior 
MNJ Mts 30-1-1 has 29-33% Ni and Co; 0.5-1% - Mts; 0.5-1% - there is Fe, the rest is 
copper. 
Bronzes are divided into 2 types: a) pewter; b) how are you? 

---

86 
Tin bronzes have a high anti-friction-frictional wear resistance, are resistant to 
creep, are resistant to cold, and are not magnetic. Disadvantage is tendency to 
formation of voids in casting. 
When alloyed with phosphorus, mechanical, technological and antifriction 
properties increase . If lead is added ; density increases, antifriction increases; cutting 
becomes easier; but the mechanical properties deteriorate . Zinc improves 
technological properties , iron (0.09%) improves mechanical properties . If the level of 
alloying is exceeded, the corrosion resistance and technological properties will 
suddenly decrease. 
Control questions: 
1.
magnesium and its alloys ? 
2.
cast magnesium alloys ? 
3.
Define refractory alloys? 
4.
Deformable Magnesium Alloys ? 
5.
copper and its alloys ? 

---

87